In this study , fluoborte solution consisting of lead fluoborate, tin fluoborate and cupric acetate was used. By addition of small amount of Cu+= ion to the solution, the Cu content of deposition layer was almost controlled less than 5%. The amount of Cu in deposition layer was almost constant without any influence of Pb++ & Sn++ in the solution, and the amount of Pb was increased by the increase of total concentration of Pb++ +Sn++ in the solution, and the amount of Pb was increased by the increase of total concentration of Pb++ +Sn++ in the solution . Agitation of plating solution & low current density result in the increase of Cu content. Analyzing of microscopic structures and etching tests of the deposited alloy, it was believed that the alloy had a lamellar structure consisting of copper rich lamellar and lead rich layer.