The objective of this study is to determine an appropriate cement of soil-cement in which silty soil of salty tidal flat with low plasticity was used. Physical, chemical and mechanical tests were conducted to find out the standard properties of the soil to be used. Various cement contents used in this test were 8%, 10%, 12%, and 14%, and the compressive strength was tested after 7 days and 28 days of standard curing in the above each cement content respectively. The results obtaind are summarized as follows. 1. As the cement content was increased from 8% to 14%, Maximum dry density (M.D.D.) and optimum moisture content (O.M.C.) were not changed remarkably. 2. Density of soil-cement was directly proportional to cement content and inversely proportional to water content. 3. OMC was generally decreased in proportion to the increase of cement content. 4. Compressive stranth was directly proportional to centent and inversely proportional to water content. 5. In freezing and thawing test, maximum loss of 10% in the total Weight was found on the 8% cement mixture. and This loss was rapidly decreased to 2% when the Cement content of the mixture was more than 10%.