In order to obtain the superior refractory setter having better spalling resistance, cordierite was synthesized from domestic raw materials. Raw mixtures were fired between 125$0^{circ}C$ and 140$0^{circ}C$, and qualitative determination of crytallization was investigated by x-ray diffraction analysis. The results obtained are as follows; 1) The optimum batch composition of synthesized cordierite is 80.5% of Hadong kaolin (pink), 14% of Kyulsung tromolite talc and 5.5% of magnesia clinker, and the firing temperature is 1375$^{circ}C$. 2) The composition of the refractory setter which exhibits the best values for the thermal properties is 40% of synthesized cordierite, 30% of kaolin chamotte(contains more than 60% of mullite), and 30% of Japanese clay. 3) The optimum particle size distribution of ternary mixture consists of 50% of coarse articles (3.327-1.168mm), 25% of intermediate particles (1.168-0.208mm) and 25% of fine particles (0.208-0.000mm).