The boronizing method using ferroborn and NaBF4 powder mixture was studied for surface hardening of medium carbon steel. This boride layer was compared with a boride layer that was formed in ferroboron and KBF4 powder mixture. The frequency factor and activation energy were discussed in this paper. The main results obtained can be summerized as follow. 1) The optimum range of NaBF4 content is 10 to 15% of weight to obtain a thick and dense boride layer. 2) The depth of the boride layer was approximately expressed by the following equation : {{{{d=100 exp (-18,000/RT) SQRT { t} }} 3) The oxidating resistance of boronized steel proved to be good at 800$^{circ}C$ but almost unacceptable near at 900 $^{circ}C$. 4) The NaBF4 effect was the same as that reported for KBF4.