In this study several kinds of spun silk yarn-synthetic filament compounded yarn was manufactured, and several fabrics woven from above mentioned silk compound yarn for evaluation of serviceability as clothing materials. The following results were obtained: 1. Degumming agents are in the order of sodium silicate, sodium hydroxide, sodium carbornate, soap and water. 2. When the concentration of sodium hydroxide is exceeded 3%, degradation of floss silk property is resulted because of excessive dissolving out of silk protein. 3. Degumming effect is much improved by concentration of degumming agent and less by its treating time. 4. Simultaneous application of more the 2 kinds of degumming agent is desirable for improvement of floss silk. 5. Application of natural organic acid brings very good results in keeping original scooping and color of the silk. 6. Load and elongation it increased by compound with synthetic filament yarn. 7. Even the evenness of compound yarn is largely dependent on the quality of floss silk and extent of degumming, the C.V.% of silk compound yarn in the experiment was 8-12%. 8. Single bath dyeing technique was impossible for their cloth, and dyeing was performed in 2 bath system separately for silk and synthetic fiber. 9. Shrinkage ratio due to the dyeing of fabric was 23% in case of polyester and spun silk fabric. 10. The final woven cloth can be applicable to (a) Blouse in care of thin cloth (compound silk fabric) (b) Korean costume for women in case of thick cloth. (compound hand spun silk fabric)