The structure of anodic aluminium oxide films formed in 2% oxalic asid at constant temperature was studied by the oid of the transmission and replica electron microscopy. Far the initial stage of oxidations, it is observed that pores are initiated from lattice defects as subgrain boundaries, and then spread radially. Some pores merge each other and the others cease to grow until the current density reaches to the steady state. The pore diameter and the cell size are proportional to the anodizing voltages, and it is considered that the pore initiation and growth are largely controlled by the field - assisted oxide dissolution.