Instead of barium carbonate, domestic barite was used as the flux in manufacturing theinsulating porcelain. To avoid the problems arising from the decomposition of barite in the body during firing, BaO.$Al_2O_3$ was synthesized at $1300^{circ}C$ for 5 hours. synthetic BaO.$Al_2O_3$ was mixed with other materials such as kaoline, alumina, clay, dolomite. The RO content (CaO. MgO. BaO) of the batches was varied from range of 4 to 14wt. % at 2wt. % - intervals, and firing temperature was varied from 1280 to 140$0^{circ}C$-at 4$0^{circ}C$ intervals The properties such as water absorption, bulk density. mechnical strength, specific resistance, and linear shrinkage were measured. The body containing 12 wt.% of RO content showed the satisfactory for the application in the Fixed Carbon Film Resistor.