The purpose of this study was to evaluate the color penetration of cavity margin with composite resin restorations in some Korean foods substance-soy sauce and hot bean paste. Fifty specimans which were extracted caries free third molar of young adults recently. All of the prepared 100 cavities were filled with two kinds of composite resin (Hipol$^{(R)}$and Restodent$^{(R)}$). The experimental specimans were divided into five groups by the following procedures. Group I : Filling of composite resin and polishing. Group II : Filling, polishing, etching of cavity and sealing. Group III : Etching, sealing, filling and polishing. Group IV : Etching, sealing, filling, polishing, and repeated of etching of cavity margin and sealing. Group V : Etching, sealing, filling, polishing, and sealing again without etching. Before examination, the restorated teeth were subjected to thermal cycling ($4^{circ}C$ and $60^{circ}C$). All the specimens were immersed in soy and 30% hot bean paste solution under $37^{circ}C$ incubator during six weeks. Then, the specimens were sectioned bucco-lingually through the center of two restorations with diamond disk and examined under a. metallographic microscope. (Union 6617 U.S.A.) Thereafter, the degree of color penetration was calculated and analyzed. The obtained results were as follows: 1. The color penetration was the lowest in the procedure of Group III which was acid etching, sealing, composite resing filling, and polishing. 2. The color penetration occured in soy and hot bean paste, but the degree of penetration was not so significant statistically between them. 3. The degree of color penetration was not so significant statistically between Hipol$^{(R)}$ and Restondent$^{(R)}$.