The mechanical and microstructural properties in high heat input welds of home-made SM 50 high strength steels were investigated and compared with the manual shielded metal arc welds. Also, the fracture toughnesses of the simulated weld-bonds with various thermal cycles were quantatively examined in order to provide the basic data for further development of the high strength steels for high input welding. Main results obtained are as follows. (1) The embrittlement degree and the coarse grained region in high heat input welds appear to be extraordinarily large compared with the manual shielded metal arc welds, while the difference in change of nicrohardness is not so large in both welds. (2) The embrittleness in high heat input weld-bonds is mainly affected by the size of coarse grain rather than the microstructure. (3) The fracture toughness in high heat input weld-bonds can be improved by controlling the cooling rate from 800.deg.C to 500.deg.C rapidly.