Quantitative analysis have been carried out on the micro-cracks on the surface and into the depth of unnotched smooth mild steel specimen under cyclic stains by rotating bending fatigue tests. Some of the results are; (1) Cracks initiate at the early stage of fatigue life N$_{I}$/ N$_{f}$=10 to 20%, and propagate during the rest of fatigue life. (2) Coalescence of highly crowded small fatigue cracks of random distribution seems to induce the final fracture at higher stress level. (3) The curves of crack initiation and the equal crack length on the graph of stress versus number of cycles are parallel to the S-N curve. (3) The curves of crack initiation and the equal crack length on the graph of stress versus number of cycles are parallel to the S-N curve. (4) The distributions of micro-surface crack length and depth show the composite Weibull distributions which are approximated to two straight lines separated by the value of transient region between stage I and stage II crack.k.k.