The objectives of this paper were to measure the bond strengths of reinforced concrete in which the steel rods were coated with five different kinds of anticorrosion paints, and to compare their prevention effects in salt water. The paints used in the study were epoxy resin I . II . III, Z.R. P., and silicone resin, which were applied at rates recommended by the manufacturers. The bond strengths were measured on the 7-, 14-, and 28-th days after molding. Corrosion conditions of coated steel plate under fresh water, seawater, 10 % salt water, and 20% salt water, were inspected every month during four months test peoriods, respectively. The results obtained from tests are summarized as follows: 1. Paint-coating may reduce the bond strengths of reinforced concrete. Silicone resin paint showed some 20% reduction in the strength compared to those without the paint. However, the other paints seemed not to significantly affect the strength. 2. Picture analyses showed that epoxy resin I and II significantly prevented corrosion steel plates in seawater. Epoxy resin I and silicone resin coating did not do a good job in corrosion prevention. Z.R. P. paint was found to be moderate as preventive coating paint. 3. Varying soluble salt contents had little effects on the corrosion prevention of tested paints. 4. Epoxy resin I and II were found to be appropriate as a coating material to prevent the corrosion of steel rods in seawater. Z.R.P. may also be used for the purpose.