The purpose of present study is to find the structures physical properties and their inter-relations in the system of (60-x) PbO.xMO.$40B_2O_3$ glasses where MO represents for ZnO and CdO. The experiments such as differential thermal analysis infrared spectral analysis X-ray diffraction analysis density and thermal expansion measurements have been done. From infrared spectral analysis the structural units of glasses and the corresponding crystallized glasses were com-posed of $BO_3$ triangles and $BO_4$ tetrahedra. These basic units found in $PbO-B_2O_3$ binary glass system did not charge even though the divalent metallic oxides were substituted for PbO. The structures of these ternary glasses were more coalescenced than $PbO-B_2O_3$ binary glass system. This fact was supported bydecrease in thermal expansion coeffici-ent and molar volume with substitution of divalent metallic oxide for PbO. Crystalline phases obtained from the heat treatment of the $PbO-ZnO-B_2O_3$ glasses were 4PbO.2ZnO.$5B_2O_3$ PbO.2ZnO.$B_2O_3$ and unknown phases.