The effect of aging coprecipitate obtained by the reaction of mixed solution 1.1 mol FeCl-0.1 mol $BaCl_2$ and 4.0 mol. NaOH-1.0 mol $K _2 CO_3$ on the synthesis process of Baferrite $(BaFe_{12}O_{19})$ was investigated by means of DTA, TGA, XRD and electron microscope. The no-aged coprecipitate seems to be the aggregate of amorphosus $Fe_3$ .$nH_2O$ and (1-X) $BaCO_3$.$xBa(OH)_2$, but the 30 days-aged to be composed of crystalline $Fe_2O_3H_2O$ and $BaCO_3$. The decomposition temperature of $BaCO_3$ in the coprecipitate increases from 400-$700^{circ}C$ to 700-90$0^{circ}C$ with increment of aging-time. In the no-aged coprecipitate Ba-ferrite is synthesized through the surface reaction of amorphous Fe_2O_3$ and skeleton crystal BaO at 800-90$0^{circ}C$ with more compact crystalization. During calcination of the 30 days-aged coprecibitate the intermediate phase BaFe_2O_4$ is formed at 600-$700^{circ}C$ and completely transformed to Ba-ferrite at 800-90$0^{circ}C$