The purpose of this dissertation is to increase oxidation resistance for Polybutadiene & Polyisoprene, and to investigate the energetics of inhibited oxidation of Polybutadiene & Polyisoprene stabilized with various types of antioxidants using DSC. The results of the study are as fellows: 1. In the DSC SCREEN for the onset temperature of oxidation, Polybutadiene was faster than Polyisoprene for the samples containing no antioxidant in air. 2. In the DSC evaluation for Polybutadiene, Recipe BG-4 with 2.0phr compounds of antioxidant was the best effective, and Recipe BS-4 with 2.0phr compounds of antioxidant was the worst effective, and the degrees of effect of antioxidant were exhibited in the ranking of G-1, D, BHT, and SP, roughly. 3. In the DSC evaluation for the Polyisoprene, Recipe IG-4 with 2.0phr compounds of antioxidant was the best effective, and Recipe ID-4 with 2.0phr compounds of antioxidant was the worst effective, and the degrees of effect of antioxidant were exhibited in the ranking of G-1, SP, BHT, and D roughly. 4. In the study on enthalpy which depends on exothermal reaction, the enthalpy of Polyisoprene was gloater than that of Polybutadiene. However, the problem was not solved completely, and it needs further studies.