This study was undertaken to evaluate the effects of varnish application and thermocycling on the marginal leakage. 240 cavities of Class V were prepared on the 120 extracted premolars, and the cavities were filled with amalgam, Heliosit$^{(R)}$, and Hipol$^{(R)}$ after application of Copalite$^{(R)}$ or Duraphat$^{(R)}$. All specimens were immersed in methylene blue solution for 24 hours after thermocycling at $4^{circ}C$ and $60^{circ}C$, embedded in acrylic resin, and sectioned with low speed saw into two parts. The sectioned specimens observed with the metallurgical microscope. The following results were obtained: 1. The marginal seal was more effective in the amalgam-filled cavities after application of Copalite$^{(R)}$ threetimes or an application of Duraphat$^{(R)}$ varnish than in those without varnish applications. 2. Of the composite resin-filled cavities, the leakage of the varnish applied cases showed much more than without application. 3. There was no significant difference in the effect of marginal sealing between Copalite$^{(R)}$ and Duraphat$^{(R)}$ applications. 4. There was a significant difference in the degree of the marginal leakage of amalgam-filled cavities between the groups of thermocycling times, but no significant difference in the resin-filled cavities. 5. There was no significant difference in the degree of the marginal leakage between the Heliosit$^{(R)}$ and the Hipol$^{(R)}$ resin-filled cavities.