An attempt is made to predict the wear behavior of ion-nitrided metal, when wear arises from asperity interactions. The analysis demonstrates that wear mechanisms are not inconsistent with observed behavior, indicates and approaches to a better appreciation of the effects of such factors as nitrided layer formation and surface topographical features. It was found on ion-nitriding that penetration rate and case development are faster and wear properties of the final product are more improved than conventional gas and salt-bath methods of nitriding.