$eta$-Sialon synthesis was investigated via the simulataneous reduction and nitriding of Wando pyrophyllite. When Wando pyrophyllite-graphite-$Si_3N_4$ seed mixture was heated at 135$0^{circ}C$ for as long as 10 hours in 80% $N_2$-20%$H_2$ atomsphere $eta$-$Si_3N_4$ solid solution was mainly formed together with a small amount of $alpha$-$Si_3N_4$ The value z of the forming $Si_{6-x}Al_2O_2N{8-z}$ was decreased with heating time.