Carburizing of a 12%Cr steel containing 0.6%Si was performed at 950$^{circ}C$ for various times, and the microstructure, hardness and the water characteristics of the carburized chromium steel were examined. The results obtained in this study are as follows: 1. Carbide-dispersed layer (CD layer) with fine dispersion of $Cr_7C_3$ in martensite matrix was formed by carburizing. The radius and amount of the carbides in the surface region of CD layer were about 0.3${mu}m$ and 35% by volume, respectively. 2. Chromium steel carburized and quench-tempered showed better wear resistance and hardness than ordinary high chromium tool steel. It is concluded from these results that fine dispered carbides are very effective in improving wear resistance and hardness.