As a part of the studies on adsorptive properties of Korean halloysite clays, Hadong white clays of premium grade were examined for geometric pore structured by mercury porosimetry and for specific surface areas by nitrogen adsorption according to the BET procedure. Three size fractions of the native clay sample were derived from passage BS #100, #200 and #325 meshes, respectively. Several parameters lhus observed in relation to the pore structures are shown below: 1. The size fraction of BS #100, #200 and #325 show internal pore volumes of 25.3, 30.2 and $35.0m^2g^{-1}$, respectively. 2. In the distribution curves of the cumulative pore volume against pore diameter, it has been shown that the larticle sizes, the steeper the distribution over the larger ranges of pore diameters. The converse is true the smaller particles. 3. Internal pore areas increase with decrease in pore sizes. It follows that the pores having diameters of $leq$0.1$mu extrm{m}$ are responsible for more than 90% of the total pore area. 4. The behaviour of nitrogen adsorption can be best described by BET type IV isotherm. Further, the hysteresis loops of the adsorptiondesorption curves become narrower with decresing particle sizes. 5. The specific surface areas observed for the fractions of BS #100, BS #200 and BS #325 are 34.6, 35.4 and 43.2m $^2g^{-1}$, respectively. and the calcined clay of BS #325 has a specific surface area near $30.4m^2g^{-1}$.