The bond strength of metal to ceramic sealing in Mo-Mn metallizing was investigated by examining the effects of flux composition in alumina ceramics particle size of molybdenum metal powder wet hydrogen atmosphere and temperature in metallizing. The maximum bond strength was obtained when the glass phase filled almost all the microstructural cavities around the interfacial area with few micropores. Such a favorable microstrcutre waas formed and maximum bond strength was observed between 130$0^{circ}C$. Also the metal to ceramic bond strength was increased using finer molybdenum metal powder than coarse powder. When content of $SiO_2$ in the flux of alumina ceramics was constant metal to ceramic bond strength was improved with increasing the ratio of CaO to MgO in the flux.