The microstructure of zine electrodeposits was investigated by using zinc sulfate solution in still bath. The cathode current efficiency decreased with increasing current density, and decreasing temperature. The preferred orientation of the zinc electrodeposits changed from (10.3) texture to(10.${ell}$)-(00.1)(${ell}$=1, 2, 3) texture through (10.2)-(10.3) preferred orientation with increasing cathode over potential. The surface morphology of zinc electrodeposits changed from the dendritic growth with granular crystallites to the blocks of hexagonal crystallites packed together with increasing current density. The microstructure of cross section of the above deposits are the rough granular structure and columnar structure respectively.