This paper was studied about the influence of oxidized films on workability in cold pressure welding. In preceding studies, the principal foci of the studies about pressure welding were considered several factors(surface manufacturing methods, surface roughness, pressure welding speed and surface temperature). But the influence to the growth of oxidation have hardly known well. So the purpose of this paper consists in solving the question above and proposing the optimal states of the pressure welding. Therefore the results obtained is as the following; When the oxidation time is within about 2 minutes, the bonding strength is very good after surface manufacturing of the neighboring to be bonded. The more surfaces are fine the more bonding strength is excellent. Above all, the optimal condition of cold pressure welding is the state that the characteristic value is 38% with smooth surface and without oxidation.