Extensive studies have been made of the effects of freeness and the calcium carbonate on the physical properties of hand-sheets from commercial flax, kenaf and NBKP. As freeness increased, the hand-sheets from the pulps above showed higher retention rate of calcium carbonate, brightness, opacity and tensile strength but lower value of porosity. Among these, the retention rate(46%) showed the highest value In kenaf, the porosity(205 c.u.) in flax, and the opacity(67%) and the tensile strength(2.8kg) in NBKP respectively. Under the constant freeness, retention rate of calcium carbonate in hand-sheets increased until 1.4 times pulp weight was added in flax and kenaf but, in NBKP, decreased from the beginning of 0.8 times with the highest retention rate. Results above led to higher porosity, opacity, brightness but lowered tensile strength. Mixed pulp(Kenaf+ NBKP) showed higher retention rate than each pulp. Pictures of X-ray diffraction and scanning electron microscope demonstrated that both of domestic and foreign calcium carbonates were calcite of spindle form. The brightness of foreign calcium carbonate was higher by 295 than that of domestic one. The average particle size of calcium carbonate was 2.1 U m(domestic), 3.6 U m(foreign).