Manganese in the Anode slime and the paste-positive material of waste-dry cell was recovered by leaching with the hydrochloric acid solution. The impurities (Zn, Fe, Pb), co-leached with manganese were removed from the leached solution prior to electrolysis by hydrometallurgical techniques such as the neutralization with ammonium hydroxide and cementation on manganese powder. The electrodeposition of manganese from the purified chloride solution with sodium selenate was performed. Cathode current efficiency was found to be affected significantly by the concentration of sodium selenate and ammonium chloride salt, bath temperate, current density and PH. The current efficiency of about 88.7% was obtained by electrolysis manganese chloride solution with sodium selenate (0.1/g) at 10$^{circ}C$.