Codeposited of boron nitride(BN) particle dispersed into electroless nickel-phosphours (Ni-P) and nickel-boron(Ni-B) platings were studied for the purpose of developing the wear resistance and lubricity. BN can be codeposited from electroless nickel plating bath with $NaH_2PO_2$ and $NaBH_4$ as the reducing agents. Most dispersolids were distributed uniformly in the Ni-P and Ni-B matrix. Abrasion loss decreased with increasing amount of codeposits and reached a constant value 2.4 percent by volume percent of BN particle. The wear resistance and the friction coefficient of the heat treated BN composite coatings were improved about three times than that of as-coatings. The BN composite coatings were more wear resistance than hard chromium. Ni-B-BN composite coatings showed lower wear resistance and friction coefficient than Ni-P-BN. The BN content of the deposite was found to be 2.4 v/o for these optium conditions.