The purpose of this study was to measure penetration of dye stuff (2% Methylene blue, 2% Hematoxylin, 2% crystal violet and 2% safranin-O) on unfilled resin (Lang Dental MFG Co.) Hipol (Boopyung Dental Chemical Co. Macrocomposite resin) Durafill (Kulzer, Co. Microfilled Composite resin) and Heliosit (Vivadent Co. Microfilled Composite resin) The unfilled resin with dough stage was inserted into plastic tuble (5mm in diameter and 4mm in height) with condensation force of 1000 gr, 2000 gr and without condensation force. Hipol mixed on the mixed pad was inserted into the plastic tube by the same method as the unfilled resin. The microfilled resins which were Durafill and Heliosit were polymerized for 60 seconds with the visible light on each surface of the plastic tube which was upper and lower, under condensation force of 1000 gr, 2000 gr and without condensation force. All specimens were stored in the air for 24 hours, then specimens were immersed in the various kind of dye solution for different period of time (1 hour and 24 hours). These dye-treated specimens were polished horizontally until removing 0.5mm of each surface on the emery paper (#1000), and the dye penetration in the polished surface was measured under the digital microscope (Japan Fosuh). Following results were obtained 1. The penetration of dyes was the most excessive in Durafill and was not influenced on the condensation force and the period of immersion time. 2. All dyes were penetrated into Hipol, and Crystal violet was penetrated most excessively in all dyes. 3. The penetration of dye in all resins was not influenced by the period of immersion time and condensation force. 4. There was no evidence of dye penetration in unfilled resin.