The surface rolling, one of the plastic working processes, provides good surface roughness with the reduction of diameter and the increase of surface hardness. In this study three Nachi 6000ZZ bearing were used for surface rolling on ductile cast iron. The results obtained are as follows; (1) The good surface roughness can be obtained with roller surface radius of curvature of 24mm after the 2nd rolling. (2) The surface roughness of ductile cast iron was 0.48.mu.mRmax by the contact pressure of 140kgf/mm$^{2}$ and surface hardness was Hv 395 with roller surface radius of curvature of 24mm after the 2nd rolling. (3) The reduction of specimen diameter of ductile cast iron were -12.8.mu.m due to rolling. (4) Within the diameter variation of -11.mu.m, surface roughness and surface hardness were increased, but at the range of exceeding -14.mu.m of the diameter variation the surface roughness became worse and the surface roughness became worse and the surface hardness was increased. (5) Dynamic contact area was about 25% to 30% of static contact area. The calculated contact pressure showed a good agreement with the experimental contact pressure.