This thesis is to improve the mechanical properties of carbon steel by the ion-nitriding, and post-heat treatment. The structures of ion-nitrided SM45C steel were changed to martensite by quenching from 730.deg. C and 800.deg. C. And then a few of the quenched specimens was tempered at 200.deg. C for 120 min. The emphasis in this study is focussed on Comparison of hardness and fatigue strength with the ion-nitrided steel. The results obtained are summerized as follows. 1. To improve the hardness and fatigue strength of ion-nitrided steels, it is effective to under take diffusion treatment for a short time at the austenite temperature(800.deg. C). 2. If ion-nitrided steel is heated for a long time at high temperature, de-nitriding occure. 3. The quenching treatment after nitriding on the carbon steel is necessary to improve the mechanical properties of the steels.