This paper describes weldability of dissimilar metal plates with YAG laser for the use of a small-size electronic spring parts. Effects of welding conditions, combination of plates, thickness of upper plate are examined in relation to welding strength and microstructure of welded region. The obtained results are summarized as follows. Welding defects such as cavity and crack showed a tendency to easily occur in the case where 1) pulse duration is short, 2) laser power is high, 3) PBS plate with high thermal diffusivity is used for lower plate. Among these defects, the occurrence of cavity cased a drop of welding strength. This results from the reduction of welding area between upper and lower plates. In SK-5/SUS304 plates (thickness: 0.2/0.4mm/, welding strength was the highest in welding conditions: laser power is 30J/pulse, pulse duration 9ms, amount of defocus +2mm.