The effects of flux KCl and dopants, La2O3 and Ta2O5, on the PTCR characteristics in molten salt synthesized BaTiO3 have been studied. The resistivity of BaTiO3 at room temperature decreases with increasing amount of dopant La2O3 up to 0.2 atom%, and then increases with La2O3 content. In case of dopant Ta2O5, it increases with increasing amount ofthe dopant. These results could be explained by observation of the microstructure and defect equation. From the results of complex impedance-frequency characteristics, the grain resistances are almost same but the resistances at the grain boundary are quite different.