The physical and dielectric properties of complex perovskite compound Sr(Mg1/3Nb1/3)O3-Ba(Mg1/3Nb2/3)O3-Ba(Mg1/3Ta2/3)O3(BMT) system were investigated as a function of composition. As the mole ratio of BMN was increased, lattice parameter ratio c/a was slightly increased, and density was increased in SMN-BMN system. However, in BMN-BMT system, lattice parameter ratio c/a and density were decreased with increasing the mole ratio of BMN. Dielectric constant, dielectric loss at $25^{circ}C$ and 100kHz, and temperature coefficient of resonant frequency, the dependence of temperature in capacitance were increased with increasing the mole ratio of BMN in SMN-BMN-BMT system. These result can be explained according to the degree of order=disorder and dielectric constant.