Recently with the rapid development in marine and shipbuilding industries such as marine structures, ship, and chemical plants, there occurs much interest in the study of corrosion fatigue characteristics was closed up an important role in mechanical design. In this study, the 5086 Al-Alloy was tested by used of a rotary bending fatigue tester and was investigated under the environments of various specific resistance and air. The specific resistance, as a corrosion environment, was changed 15, 20, 25 and 5000$Omega$.cm. The corrosion fatigue crack initiation sensitivity was quantitatively inspected for 5086 Al-Alloy in the various specific resistance. The experimental constants of Paris rule were examined in the various specific resistances, and the influences of load and corrosion with affect the crack growth rate were compared with. Main results obtained are as follows: (1) Number of stress cycles to corrosion fatigue crack initiation delaies and corrosion fatigue crack initiation sensitivity decreases with the increasing for the specific resistance. (2) The experimental constant m of Paris rule decreases with the decreasing for specific resistance. Hence the effect of corrosion is more susceptible than that of stress intensity factor. (3) The corrosion fatigue crack of 5086 Aluminium Alloy appears intergranular fracture. (4) Corrosion sensitivity is decreased with the increasing stress intensity factor and is nearly uniform when stress intensity factor is over 40kg.mm super(-3/2)