The variation of Composition and the microstructure of Zn-Ni alloy electrodespposits were investigated to the electrolysis conditions chloride bath. The codeposition mechanism is of the equilibrium type in the electrolysis condition of the high temperature(6$0^{circ}C$)and high flow rate (1.2-3.0m/sec). The(411, 330) perferred orienation was mainly developed in the Zn-Ni electrodeposir with ${gamma}$-phase structure, while the(422.600) orientation was closely related to the commposition and the structure of the alloy electrodeposit.