The purpose of this paper is to investigate on the optimum coating thickness layer of TiC-Al$_2$O$_3$ coated cemented carbide tool. Chemical Vapor Deposition (CVD) of a thick film of TiC-A1$_2$O$_3$ on a cemented carbide produces an intermediate layer, $1.5mutextrm{m}$, 4.5${mu}{ extrm}{m}$, 7.5${mu}{ extrm}{m}$ 10.5${mu}{ extrm}{m}$, 4 kind of TiC between the substrate and the $1.5mutextrm{m}$ constant thick A1$_2$O$_3$ coating. Experiments were carried out with the test relationship between coating thickness and shear angle, surface roughness, cutting force, microphotograph of crater wear, flank wear, tool life. From the experimental results, it was found that the optimum coating thickness of TiC-A1$_2$O$_3$ is 6${mu}{ extrm}{m}$. Although the coating thickness layer 9${mu}{ extrm}{m}$. 12${mu}{ extrm}{m}$ have a much loger tool wear than an 3${mu}{ extrm}{m}$, 6${mu}{ extrm}{m}$ coating tool in cutting condition feed 0.05mm/rev, and the condition of feed 0.2mm/rev, 0.3mm/rev has upon in the shot time phenomenon of chipping.