Corrosion fatigue crack propagation behavior of duplex stainless steel weldments in substitute ocean water was investigated to evalulate effects of micro-structural change and residual stresses. Fatigue crack propagation rate was found influenced markedly .alpha./.gamma. phase ratio but little by residual stresses. Fatigue crack propagation rate is higher in the corrosive environment than in room atmosphere. The crack propagation rate estimated by the measurement of striation spacing was higher than that, obtained by crack length measurement in low .DELTK.K region. At hight .DELTK.K region, however, both crack propagation rates were found to be identical.