Basic investigation for the flexural strength and water stability of hardened cement pastes using ordinary portland cement with water-soluble polyer (hydroxypropyl methyl cellulose ; HPMC) was carried out with 0.2 of water cement ratio. For molding of the specimen, the paste was mixed by twin roll mill. According to increase in the content of HPMC, the setting time of cement paste was delayed and the flexural strength was increased. The maximum flexural strength of hardened cement paste with 5.0wt% of HPMC was about 330 kg/$ extrm{cm}^2$. The expansion of the hardened cement paste immersed in water was increased with the content of water soluble polymer(HPMC). Consequently, the strength and the water stability of the hardened cement pastes were remarkably reduced by the expansion of them.