To investigate the influence of $TiCl_4$, $N_2$ inlet fraction on the TiN layer, TiN film was deposited onto the STC3 and STD11 steel from gas mixtures of $TiCl_4/N_2/H_2$ by the radio frequency plasma assisted chemical vapor deposition. The films were deposited at various $TiCl_4$, $N_2$ inlet fractions. The results showed that the film thickness was increased with $TiCl_4$ inlet fraction. However, while the thickness was increased with $N_4$ inlet fraction under 0.4 the thickness was decreased with increasing $N_2$ inlet fraction over 0.4. The density of deposited films was varied as $TiCl_4$, $N_2$ inlet fraction and its maximum value was about $5.6g/cm^3$. The contents of chlorine were increased with increasing $TiCl_4$ inlet fraction and nearly constant with increasing $N_2$ inlet fraction.