This paper is studied to know corrosive wear mechanism of STS304 steel on atmospherical temperature against mating material as the same. The corrosive test was carried out by rubbing the annular surface of two test pieces in distilled water and NaCl aqueous solution. The corrosive wear mechanism was investigated by S.E.M. The experimental results show that there is one Lcr transferring from severe wear to mild wear on change of NaCl concentration and atmospherical temperature, and which is the other still remaining in server wear state. It was found that the critical sliding distance Lcr shorten with increasing NaCl concentration but it is longer with ascending atmospherical temperature and the mild wear state still continues under the condition of high generation rate and elimination rate of the corrosive product. Considering upon the result, the model of corrosive wear mechanism is proposed.