Fine Si-Al-OH-C coprecipitate powders were prepared from Si(OC2H5)4, Al(i-OC3H7)3, and carbon black by a hydrolysis method before fabrication of Sialon-SiC composite powder by carbothermal reduction at 1350$^{circ}C$ for 10h under N2/H2 mixed atmosphere. The characterization of the synthesized Sialon-SiC composite powders was performed using XRD, BET, SEM, TEM and particle size analysis methods. The average particle size and specific surface area of the synthesized Sialon-SiC composite powder were 0.13$mu extrm{m}$ and 20.1㎡/g, respectively when Z=1 and N2 : H2=50 : 50.