Cordierite powders were prepared from Si(OC2H5)4, Al(OC3H7i)3 and Mg(OC2H5)2 by the sol-gel method. Two different methods were applied for producing fine and homogeneous powders. One is that Si(OC2H5)4 with a lowr rate of hydrolysis was partially hydrolyzed and then Al(OC3H7i)3 and Mg(OC2H5)2 were mixed and reacted. The other is based on the simultaneous hydrolysis of these metal alkoxides using i-C4H9OH which retards the rate of hydrolysis of Al(OC3H7i)3 and Mg(OC2H5)2. It was confirmed that ifne and homogeneous powders were obtained from both methods. Also these powders were calcined at four different temperatures during two hours. X-ray diffraction patterns show only ${mu}$-cordierite phase at 1000$^{circ}C$, ${mu}$-cordierite and ${alpha}$-cordierite phases at 1100-1200$^{circ}C$ and ${alpha}$-cordierite phase at 1300$^{circ}C$ respectively.