Melt-textured growth of the YBa2Cu3O7-x phase from a supercooled melt created locally aligned, barshaped grains of the orthorhombic 1-2-3 phase. Based on all the observed phenomena, the gross mechanism of the melt-textrued growth of YBa2Cu3O7-x on the (100) plane of MgO was delineated by three basic patterns of reactions. These are : (ⅰ) formation of the aligned 1-2-3 phase and the Y-rich 2-1-1 phase at the bulk region away from the (100) plane of MgO ; (ⅱ) formation of the Cu-richprecipitates at the interfacial region by the selective interface-induced precipitation of the liquid phase ; (ⅲ) condensation reaction of the entrapped Cu-rich vapor with Mg atoms during the initial stage of rapid cooling from 130$0^{circ}C$ to 98$0^{circ}C$.