The effect of primary solidification phase on the solidification cracking sensitivity, corrosion resistance and toughness at cryogenic temperature was investigated for the austenitic stainless steel welds. The conclusions were summarized as follows; 1. Soldification crack sensitivity of austenitic stainless steel welds depends on the primary solidification mode. 2. Austenitic stainless steels were very susceptible to solidification cracking in case of solidification as primary ${gamma}$ and immune when solidified as primary $delta$. 3. When the ratio of Creq/Nieq is in the range of 1.46 to 1.55, the most resistance against solidification cracking was obtained. These results agreed well with the relationship between primary solidification mode, corrosion resistance and toughness at cryogenic temperature. 4. Optimum toughness, corrosion and solidification cracking resistance can be obtained when alloys having chemical compositions described above and solidifies as primary $delta$ containing no ferrite at room temperature.