Fatigue crack behavior is studied through the two-level rotary bending test with the deep non-through radial holed notch specimens of low carbon steels(SM22C). The main factors investigated are the effects of the damage zone size around crack tip and phenomena of closing or opening of the crack tip. Obtained results are summarized as follows. Fatigue crack behavior in second level stressing slightly lower than fatigue limit is closely related to the size of damage zone produced by the first level stress higher than fatigue limit and to the phenomena of crack closing and opening for the second level stress. The non-propagating crack limit condition depends upon the crack length l$_{1}$ propagated under the first level stress and the magnitude of second level stress .sigma.$_{2}$ lower than the fatigue limit. The non-propagating crack limit condition is expressed by following eq. .sigma.$_{2}$$^{6.1}$ *l$_{1}$=7.35*10$^{6}$ [(kg$_{f}$ mm$^{6.1}$ (mm)]