The effects of compositional variation, rotation speel and pulling rate on the growth of optical quality Bi120e02(1 crystals were examined. It was found to flatten the shape of crystal-melt interface for yowing a single crystals less than about 30mm in diameter at the rotation speed of 50rpm. Diameter of crystals with flat interface was increased as the pulling rate. The precipitation of Bi40e3012 phase set limits to pulling rate of BGO crystals. Precipitate-free BGO crystals were grown under pulling rate of 2mm l hr which released the stress resulted from too hi어 Pulling rate, and from 6. IBi203·GeO2 batch composition obtained by addition of 0.1 mole Bi203 into Bi-deficient melts to fill up the deficiency resulted from gradual volatilization of Bi2O). The pale-yellow colored crystals had good quality in that dislocation density was less than 103pits/cm, and it also exhibited transmittance of 70% and optical activity of 23°/mm. and SAW velosity was measured 1700m/sec on 111 cut 110 propagating BGO crystals. The SAW filter with electrode thickness of 9.8um was fabricated by using the electron beam and dry etching technique, it makes Bi12GeO20 devices intersting for color TV IF with half device size.