The critical current density, electrical conductivity, critical magnetic field, Meissner effect, apparent density, and microstructure of YBa2Cu3O7-x ceramic superconductor prepared by polymeric precursor, while varing calcining and sintering conditions, were investigated. The best superconducting properties could be obtained from the body sintered at 93$0^{circ}C$ for 10h after calcining at 90$0^{circ}C$ for 10h, which gave 383A/$ extrm{cm}^2$ of critical current density(Jc), 96K of onset temperature(Tonset), 94. 8K of zero temperature (Tzero) 225 Oe of critical magnetic field (Hc1), 72.8% of superconducting volume fraction measured by Meissner effect and 6.28g/㎤ of apparent density.