The effects of MnO2 on the microstructure and dielectric properties of Pb(Fe1/2Nb1/2)O3 ceramics prepared by KCl-NaCl molten salt synthesis(MSS) method have been investigated. As the amount of MnO2 increased up to 0.25wt%, the density increased and the grain size decreased, while above 0.25wt%, the density decreased with the grain growth. Dielectric constant increased with increasing the amount of MnO2, and dielectric loss decreased up to 0.25wt% and then increased. This is due to the compensation effect by the substitution of Mn4+ to Fe3+ and the appearance of the second phase.