Acoustic Emission was monitored during tensile test and loading-holding-unloa-ding cycle test for two types (notched and unnotched) of CFRP specimens. AE activities showed that the fiber breakage during tensile tests depended upon the specimen geometry. We obtained new AE parameter such as the ration (damage ratio= AE events during unloading test / AE events during loading test) and the felicity ratio from which we investigated dynamic fracture process of CFRP specimens. The damage ratio of AE events was shown to be a good indicator to distinguish the generated fracture mechanism, such as fiber breakage and delamination. Also, ultrasonic testing results after loading-holding-unloading cycle test were good agreement with AE test results to detect defects or fiber breakage.