The effect of deformation temperature and manganes contents on the tensile properties of duplex stainless steels with the structure of both ferrite and austenite were investigate. For this investigation, Fe-19% Cr-5% Ni-4~8% Mn alloys were prepared. The result obtained from this experiment are summerized as follows. With decreasing deformation temperature, tensile strengths of duplex stainless steel increased. Elongation showd to be increased and then decreased after representing the highest value at specific temperature. Tensile properties of duplex stainless steel were controlled by TRIP behavior in this experimental range of austenite contents. Tensile strengths decreased with increasing Mn contents. With increasing Mn contents, elongation decreased in the high temperature region, but increased in the low temperature region. The peak temperature representing the maximum elongation were changed to low temperature and the width of peak appeared to be broaden with increasing Mn contents.