In order to investigate the cytotoxicity of composite resin in vitro, BALB / C mouse fibroblast were cultured in MEM in which silux, P-50, microrest, clearfil, amalgam and glass - ionomer, in shape of $2{ imes}9mm$ circular disk. The experiments were- performed by cell count on 4 hours, 1, 3, 6 days and the composite resin groups, amalgam, glass - ionomer were compared. 1. On the sixth day, the cellular number of resin composite groups were remarkedly reduced, in contrast, the that of amalgam and glass - ionomer group continuously increased. 2. It was only on the 4 hours that the cellular number contained in amalgam were reduced, but increased thereafter, and the cellular number contained in glass - ionomer are greater than other groups. 3. In resin group, especially between self - curing resin and light - curing resin, there is no difference in cellular number statistically (p>0.05). 4. It was amalgam where the round cell without cellular process was found on the 4. hours and on the 6 th day the cell without cellular process was found numeroulsy in resin group whereas in amalgam and glass - ionomer, like control group was contained cell forming monolayer. These result suggested that the toxicity of the self - curing and light - curing resin greater than that of the amalgam and glass - ionomer.