Eighty - eight recently extracted teeth were used to evaluate the leakage characteristics of the following retrofilling materials; amalgam, zinc oxide eugenol cement, glass - ionomer cement, and cermet glass - ionomer cement. Root canals were prepared with step - back method and obturated with gutta percha and zinc oxide eugenol sealer. Root apex were resected 2 mm from apex and class I cavities were prepared with 2 mm or 4 mm depth. The cavities were filled with above materials. After application of varnish on all surface except resected surface, the roots were placed in 1 % methylene blue solution for 6 days. After longitudinal polishing to expose cental parts of filled materials, penetrated depths of dye were measured. The results were as follws. 1. As retrofilling material, glass ionomer cement filling groups showed less leakage than the other groups except zinc oxide eugenol cement filling group(p<0.01). 2. Amalgam filling groups had greater leakage than zinc oxide eugenol cement filling group(p<0.01). 3. 4 mm depth of retrofilled cavity had no effect on leakage characteristics compared with 2 mm depth cavity(p>0.05). 4. Glass ionomer cement and cermet glass ionomer cement filling groups showed less apical leakage than amalgam filling groups. But there was no statistical significance(p>0.05). 5. There was no difference in apical leakage between glass ionomer cement filling groups and cermet glass ionomer cement filling groups(p>0.05).